| Material Status |
Development prototype |
|
| Regional Availability |
• Africa & Middle East
• Asia Pacific
• Europe |
• North America
• South America |
| Features |
• Non Halogen
• Low Smoke generation
• Low Toxicity &low corrosivity
• Environmentally friendly |
• Excellent processing
• Good heat resistance
• Good flame retardancy |
| Uses |
Wire&Cable |
|
| Forms |
Pellets |
|
| Technical Properties |
| Physical Properties |
Typical Value(Imperial) |
Typical Value (SI) |
Test Method |
| Density (23°C) |
1.48 g/cm3 |
1.48 g/cm3 |
ISO 1183-1 (ASTM D792) |
| MFR (150°C/21.6kg) |
3 g/10min |
3 g/10min |
ISO 1133-1 |
| Mooney viscosity, ML (1+4) 140°C |
49 |
49 |
DIN53523 (ASTM D1646) |
| Hardness Shore D (15 Second) |
46 |
46 |
ISO R 868 (ASTM D2240) |
|
| Mechanical Properties |
Typical Value(Imperial) |
Typical Value (SI) |
Test Method |
| Tensile Strength 200mm/min, thermoplastic |
1595 psi |
11 MPa |
IEC 60811-501 |
| Elongation at break 200mm/min, thermoplastic |
215% |
215% |
IEC 60811-501 |
| Tensile Strength 200mm/min, crosslinked ² |
1740 psi |
12 MPa |
IEC 60811-501 |
| Retention after heat ageing, 10d at 120°C |
115% |
115% |
IEC 60811-401 |
| Elongation at break 200mm/min, crosslinked ² |
130% |
130% |
IEC 60811-501 |
| Retention after heat ageing, 10d at 120°C |
91% |
91% |
IEC 60811-401 |
| Cold elongation -40°C, crosslinked ² |
45% |
45% |
IEC 60811-505 |
|
| Flammability |
Typical Value(Imperial) |
Typical Value (SI) |
Test Method |
| Oxygen index 1 |
36% |
36% |
ISO 4589-2(ASTM D2863) |
| Other Properties |
Typical Value(Imperial) |
Typical Value (SI) |
Test Method |
| IRM 902 oil, 3d at 100°C, crosslinked ² |
|
|
IEC 60811-404 |
| Tensile Strength Retention |
72% |
72% |
|
| Elongation at Break Retention |
77% |
77% |
|
| IRM 903 oil, 7d at 70°C, crosslinked ² |
|
|
IEC 60811-404 |
| Tensile Strength Retention |
76% |
76% |
|
| Elongation at Break Retention |
73% |
73% |
|
| Oxalic Acid 1N, 7d at 23°C, crosslinked ² |
|
|
IEC 60811-404 |
| Tensile Strength Retention |
93% |
93% |
|
| Elongation at Break Retention |
97% |
97% |
|
| Hydroxide sodium 1N, 7d at 23°C, crosslinked ² |
|
|
IEC 60811-404 |
| Tensile Strength Retention |
90% |
90% |
|
| Elongation at Break Retention |
97% |
97% |
|
1 measured on type IV specimen and ignition procedure A
2 measured on samples crosslinked at 120kGy.
These properties were measured once within PolyOne laboratory. However, it is mandatory that customers should conduct their
own evaluations to ensure any compliance on cable.
Data are typical values and must not to be construed as specification limits
Recommended processing parameters
| Extrusion |
Cylinder Temperatures |
|
| |
Zone 1 |
Zone 2 |
Zone 3 |
Zone 4 |
Zone 5 |
Adapter |
Head |
Die |
| Temperature (Imperial) |
266°F |
284°F |
311°F |
320°F |
329°F |
329°F |
329°F |
338°F |
| Temperature (SI) |
130℃ |
140℃ |
155℃ |
160℃ |
165℃ |
165℃ |
165℃ |
170℃ |
We recommend you not to exceed melting temperature of 170°C (338°F)
ECCOH™ 5286 is a formulation allowing PVC/PE extruders to be used.
For special extruder or application, please contact PolyOne for detailed processing information.
Pre-Drying
Our formulation is supplied in aluminium foil lined bags or octa-boxes and, providing the packaging has not been
disturbed, the formulation does not require pre-drying. If the formulation has been stored in a moist environment
over a long period then Pre-drying at approximately 70°C (158°F) for 4 hours is recommended in dehumidifying
dryers.
Colorability
ECCOH™ 5286 is a colourable formulation. A full range of polymer specific colour masterbatches are available for
ECCOH™ solutions within PolyOne.
Shelf life
ECCOH solutions are supplied in aluminium foil lined bags or octa-boxes and, based upon experience, this ensures a
minimum shelf life of one year - providing the bag is not opened and kept in a cool (0°C < Temp. < 25°C) dry
environment.
PolyOne advises customers to conduct a full homologation program on their final cable construction to
confirm acceptability. |
|